Ah, modern email tools - this link will work when clicked on:
http://www.isola-group.com/wp-content/uploads/2014/05/Developments-in-Glass-Yarns-and-Fabric-Constructions-PCB-Magazine-March-2014.pdf
-Patrick
On Sun, Jan 3, 2016 at 7:41 PM, Patrick Kelsey <kelsey@xxxxxxxx> wrote:
It only works if the 'PDF' at the end is lowercase -> 'pdf':
http://www.isola-group.com/wp-content/uploads/2014/05/Developments-in-Glass-Yarns-and-Fabric-Constructions-PCB-Magazine-March-2014.pdf
<http://www.isola-group.com/wp-content/uploads/2014/05/Developments-in-Glass-Yarns-and-Fabric-Constructions-PCB-Magazine-March-2014.PDF>
-Patrick
On Sun, Jan 3, 2016 at 7:34 PM, Lee Ritchey <leeritchey@xxxxxxxxxxxxx>
wrote:
I could not get that site to open. Did anyone else?
-----Original Message-----
From: si-list-bounce@xxxxxxxxxxxxx [mailto:si-list-bounce@xxxxxxxxxxxxx]
On Behalf Of John Phillips
Sent: Sunday, January 3, 2016 12:28 PM
To: buenoshun@xxxxxxxxx
Cc: si-list@xxxxxxxxxxxxx
Subject: [SI-LIST] Re: Glass Weave effects and Cross sectioning
Hi Istvan,
Confusingly there are two types of 1067, vanilla 1067 and 1067 "spread",
check out:
http://www.isola-group.com/wp-content/uploads/2014/05/Developments-in-Glass-Yarns-and-Fabric-Constructions-PCB-Magazine-March-2014.PDF
Hopefully that will not get mangled.
Regards
John
On 3 Jan 2016 19:57, Istvan Nagy <buenoshun@xxxxxxxxx> wrote:
pitch).
Hi,
1067 seems to be spread only in one direction. This means you can only
have low skew traces in one direction. In every big high-density board
I had we needed traces on all layers in all directions.
A table in an isola presentation shows that the glass yarn is more
than 2x thinner for 1067 than it is for 2116, and the 2116 yard is
almost as thick as the whole prepreg/core. So the glass in the 2116
can get a lot closer to the surface. This seemingly correlates to the
1067's higher resin content (75% vs 55%), and to Lee's test results.
The 2116 has smaller gap and looks more uniform from the top, so
contrary to this if the 1067 still has lower skew, then it can only be
explained with it's thinner glass that is more away from the surface,
or with the weave pitch matching with the diffpair pitch. In your
design maybe the diffpair pich was luckily matching the 1067. My
typical diffpairs have 10-11mil pich due to high density design. So,
for me maybe the 1067 (14mil pitch) would be just as bad as 2116 (17mil
Instead of anecdotes, I would like to understand the mechanism more.result every case, then it has to be communicated as a pcb design rule.
I thought the spreadness could be quantified bases on the glass
measurements. From the isola presentation the dimensions are x1=yarn
thickness, x2=yarn width, x3=pitch, then y1...y3 the same thing for
the other direction. From this I would calculate spreadness[%]>> >
MIN(x2/x3,y2/y3) . For 2116 it is 81.9%, for 1067 it is 61.8%. The
2116 is more spread, but according to Lee Ritchey it still has bigger
skew. Maybe we should not bother with spread glass, just randomly test
different fabrics? The diffpair pitch used for the tests and its
effect was not quantified. Were there any tests with mismatching pitch
conducted on 1067, or was the 1067 tested with matching pitch while
the 2116 was tested with unmatched pitch? Then its not a fair
comparison. Testing both with unmatched pitch like 10-11mil or both
with their matching values would be better. If matching gives better
Any way to quantify the effect of the cross section quality? Maybe weweave.
can use this: The glass yarn distance from surface fluctuates along the
The copper traces are on (or embedded into) the surface. The less itB*cs_quality)/2.
fluctuates the better. Not in absolute terms (mils), but as
percentage. Then cs_quality[%] = min_distance / max_distance.
Then overall quality would be: quality[%] = (A*spreadness +
A and B are weight constants, choose them to match test resultssomething.
(conducted all with matched or all with unmatched pitch).
I have only seen the yarn thickness table, I still yet to see any
cross section photo. I want to get some cross section photos for each
glass style so I can compare them, too see what exactly is going on.
This above is my speculation, it is not from existing books or
money
I am just trying to be more scientific, rather than using trial&error.
Anyone interested in developing a scientific solution?
Testing is one thing, raw test results is not what I am looking for,
but rather a method that I can apply on any material in the future.
The method has to be based on geometry-data from material vendors.
Tests have too many variables at given values, that might be different
in my designs (e.g diffpair pitch).
regards,
Istvan Nagy
-----Original Message-----
From: Lee Ritchey
Sent: Sunday, January 03, 2016 10:29 AM
To: zhangjun5960@xxxxxxxxx ; si-list@xxxxxxxxxxxxx
Subject: [SI-LIST] Re: Glass Weave effects and Cross sectioning
I have data, but it is not available for free. Spend large amounts of
doing the testing.On
-----Original Message-----
From: si-list-bounce@xxxxxxxxxxxxx [mailto:si-list-bounce@xxxxxxxxxxxxx]
Behalf Of jun zhangdatas
Sent: Sunday, January 3, 2016 6:45 AM
To: Lee Ritchey <leeritchey@xxxxxxxxxxxxx>; si-list@xxxxxxxxxxxxx
Subject: [SI-LIST] Re: Glass Weave effects and Cross sectioning
Hi Ritchey,
Do you know how much extra skew they obtain? Do they have measurement
for the skew?missing
Hope to your reply
Regards
On Sun, Jan 3, 2016 at 3:31 AM, Lee Ritchey <leeritchey@xxxxxxxxxxxxx>
wrote:
I have a client who built 400 assemblies with 2116 glass that had
dozens of 10G pairs on them. All were scrapped due to excessive skew.
Enough said!
From: Istvan Nagy [mailto:buenoshun@xxxxxxxxx]
Sent: Friday, January 1, 2016 10:53 AM
To: Scott McMorrow <scott@xxxxxxxxxxxxx>
Cc: Lee Ritchey <leeritchey@xxxxxxxxxxxxx>; SI <si-list@xxxxxxxxxxxxx
Subject: Re: [SI-LIST] Re: Glass Weave effects and Cross sectioning
Hi,
I am aware of the 3 distinct regions. The ratio of those is better for
2116 than it is for 1067, according to the 2D top view. In
ââ¬ÅBetterâ⬠I mean the 2layer (double fiber region) portion is a
lot
bigger than the other 2 (gap and 1-layer) combined. Area measurements
are sometimes provided by the material manufacturer, other times just
I qualitatively compare the 2D photos.
Although I don't know anything about the yarn cross section
difference. I thought the ââ¬Åspreadâ⬠was to reduce the 0L and 1L
regions. Maybe it is also for yarn cross section uniformity.
ââ¬Åmodern mechanically spread fabrics.ââ¬
My problem is that the same glass style from different material
manufacturers (and even the same glass style for same manufacturer but
different material names) has different mechanical spreading. And this
spreading is not really quantified anywhere. Maybe thatââ¬â¢s the
it.link.
For example 1080 is available with old style and new style. One vendor
offers 1080 in 3 different spread varieties (standard,
laser-drillable, ss-ultraspread), but the dielectric table does not
really explain which is which. One vendor has distinction like
NEA1080_N136 vs NEA1080_S013.
Maybe we should refer to glass styles as
ââ¬Å1234-vendorA-spreadBâ⬠,
instead of ââ¬Å1234â⬠. But then the fabs would not be able
identify
Er. Er
Istvan Nagy
From: Scott McMorrow <mailto:scott@xxxxxxxxxxxxx>
Sent: Friday, January 01, 2016 5:29 AM
To: Istvan Nagy <mailto:buenoshun@xxxxxxxxx>
Cc: Lee Ritchey <mailto:leeritchey@xxxxxxxxxxxxx> ; SI <mailto:
si-list@xxxxxxxxxxxxx>
Subject: Re: [SI-LIST] Re: Glass Weave effects and Cross sectioning
It's not just the gap that is important for skew reduction. What you
do not see in a 2D view from above the weave is the thickness profile
of the weave. It looks more like an elliptical bundle for older
fabrics, and like a mush more spreadout and flattened bundle for
modern mechanically spread fabrics. Because of this, there are 3
distinct regions of fabric that meld into each other, each with a
different dielectric constant when viewed down the z-axis, A high
resin region, or gap. A single fiber region, with higher Er. And a
double fiber crossover region, or "knuckle", that has even higher
<mailto:variation is pretty bad when compared to modern fabrics.
<http://teraspeed.com/images/logo-02.png>
Scott McMorrow
R&D Consultant
Teraspeed Consulting - A Division of Samtec
16 Stormy Brook Rd
Falmouth, ME 04105
(401) 284-1827 Business
http://www.teraspeed.com
On Thu, Dec 31, 2015 at 3:22 PM, Istvan Nagy <buenoshun@xxxxxxxxx
there.buenoshun@xxxxxxxxx> > wrote:
Gap is the area that is not covered with glass, there is only resin
density.You can see on the photos (in my excel file, second tab) as rectangle
empty areas. The 1067 has bigger gaps than 2116, very visible on the
photos.
So, you are saying the glass thread cross section is worse for one
material than for another? Or is where the 2 diagonal threads cross
and they somehow flatten? Do you have some drawing that explains it?
-----Original Message----- From: Lee Ritchey
Sent: Thursday, December 31, 2015 9:42 AM
To: buenoshun@xxxxxxxxx <mailto:buenoshun@xxxxxxxxx> ; 'SI' ;
scott@xxxxxxxxxxxxx <mailto:scott@xxxxxxxxxxxxx>
Subject: RE: [SI-LIST] Re: Glass Weave effects and Cross sectioning
I don't know what you mean by "gap". The reason that 2116 is not good
is that the weave results in peaks and valleys where the valleys are
filled with pure resin and the peaks are almost pure glass.
-----Original Message-----
From: si-list-bounce@xxxxxxxxxxxxx
<mailto:si-list-bounce@xxxxxxxxxxxxx>
[mailto:si-list-bounce@xxxxxxxxxxxxx
<mailto:si-list-bounce@xxxxxxxxxxxxx>
] On Behalf Of Istvan Nagy
Sent: Wednesday, December 30, 2015 7:20 PM
To: Lee Ritchey <leeritchey@xxxxxxxxxxxxx
<mailto:leeritchey@xxxxxxxxxxxxx>
; 'SI' <si-list@xxxxxxxxxxxxx <mailto:si-list@xxxxxxxxxxxxx> >;scott@xxxxxxxxxxxxx <mailto:scott@xxxxxxxxxxxxx>
Subject: [SI-LIST] Re: Glass Weave effects and Cross sectioning
Lee,
How come those fabrics yield better result than the 2116?
I have a photo album of glass fabrics from different vendors. The
1067,
1035 seems more loose than the 2116.
http://www.buenos.extra.hu/download/PCB_MATERIAL_LIBRARY.xls
For one vendor:
Measured gaps and coverage:
Fabric Xgap% Ygap%
106 74.05405405 50.48543689
1067 38.11188811 9.48905109
...
3070 14.18918919 11.26760563
2116 18.02325581 16.1849711
...
You see the 1067 has much bigger gaps than 2116.
I followed my intuitive idea that the more dense the fabric on the
photo, the more uniform it is and the least skew we get. Is there
anything wrong with my concept? Am I missing something? The percentage
of 2layer/1layer/0layer areas would determine the uniformity and
pSEC.Layer, I mean layer of glass thread on top of each other. The 0layer
gaps have dimensions of 1.3ââ¬Â¦3mil (somewhat smaller than trace
width), the weave pitch ranges from 14milââ¬Â¦26mil (several times the
trace width & diffpair gap), while the impedance controlled PCB traces
are 3.5milââ¬Â¦7mil (typically
4.5mil) wide and gaps are like 5-8mil (signal pitch 10mil). Typical
high-density high layer count designs I have seen are like this. So,
none of the fabrics have small enough dimensions to appear smooth to
the traces while having large % gaps. Therefore I relied on the gap
percentage.
Scott,
To achieve the 14mil-18mil signal pitch, you need thick prepreg/core
layers like 6-8mil thick, then the whole stackup is thicker and needs
more layers due to lower density (18mil diffpairs vs 10 mil ones take
more space). So my
18 layer 93mil stackup would become 26 layer and 200mil thick. Is this
what you are suggesting? pitch-matching would need 2x thick PCBs. Nice
theory, but I am not sure about the practicality. On the other hand...
if this is proven practice, I might consider it for my next designs.
Some form factors like ATCA have fixed board thickness, and increasing
layer count by 50% might be hard to justify. We have 200-300 10Gig
diffpairs on my latest board design, although we did not measure skew
on it, just on-die captured eye diagrams. Small company, no SI-team...
"know the fill direction of the laminate that... "
- I will keep that in mind. Somehow it has to go into the fab drawing
gerber file I guess.
So, gap-percentage, pitch-matching, documenting fill direction and
12+deg rotation...
Best regards,
Istvan Nagy
Principal Hardware Engineer
-----Original Message----- From: Lee Ritchey
Sent: Wednesday, December 30, 2015 2:05 PM
To: 'Istvan Nagy' ; 'SI' ; bbakshan@xxxxxxxxx
<mailto:bbakshan@xxxxxxxxx>
Subject: RE: [SI-LIST] Re: Glass Weave effects and Cross sectioning
Scott listed my preferred weave styles in another reply. And, yes we
do very well when we control the weave type. Better than any of the
other methods that have been proposed.
Just had a PCB with 200+ 10 Gb/S paths with the worst skew being 2
software.
-----Original Message-----
From: Istvan Nagy [mailto:buenoshun@xxxxxxxxx
<mailto:buenoshun@xxxxxxxxx> ]
Sent: Wednesday, December 30, 2015 1:35 PM
To: SI <si-list@xxxxxxxxxxxxx <mailto:si-list@xxxxxxxxxxxxx> >;
bbakshan@xxxxxxxxx <mailto:bbakshan@xxxxxxxxx> ; Lee Ritchey
<leeritchey@xxxxxxxxxxxxx <mailto:leeritchey@xxxxxxxxxxxxx> >
Subject: RE: [SI-LIST] Re: Glass Weave effects and Cross sectioning
Lee,
What is on your list of good enough weaves? Are those provide much
better results than 2116? The nicer weaves are not as available as
2116, i am talking about series production of networking and computing
boards, not test boards.
Do you expect the skew problem to be resolved mainly by glass style
selection?
Regards, Istvan, mobile
*** Sent from my BLU smartphone device *** On Dec 30, 2015 9:07 AM,
Lee Ritchey <leeritchey@xxxxxxxxxxxxx
<mailto:leeritchey@xxxxxxxxxxxxx> >
wrote:
I have had severe skew problems with 2116 at 10 Gb/S. It is not on
my list of good weaves.
-----Original Message-----
From: si-list-bounce@xxxxxxxxxxxxx
<mailto:si-list-bounce@xxxxxxxxxxxxx>
[mailto:si-list-bounce@xxxxxxxxxxxxx
<mailto:si-list-bounce@xxxxxxxxxxxxx>
] On Behalf Of Istvan Nagy
Sent: Monday, December 28, 2015 10:53 PM
To: bbakshan@xxxxxxxxx <mailto:bbakshan@xxxxxxxxx> ;
si-list@xxxxxxxxxxxxx <mailto:si-list@xxxxxxxxxxxxx>
Subject: [SI-LIST] Re: Glass Weave effects and Cross sectioning
Hello,
First getting on this topic of spread glass, everyone is looking for
the miracle spread that has no skew issues.
You can choose the glass style as a number, or to take it further and
choose a material manufacturer who promises mechanical spread or
square wave or other features too.
In reality the traditional glass styles (106, 1080) were kind of
"bad", newer more denser weaves (2116, 1501) are "better", but there
is no "excellent" fabric.
I just try to use 2116 for layers with 2Gig+ signals. So you specify
glass style, and material name, that's mainly what you can do about
it, before building the stackup for design and manufacturing.
You need to have the detailed datasheets listing all available glass
styles of your chosen material. Get glass fabric photos from your
material vendor (like Bill from NanYa), so you can see how much
difference those different fabrics (numbers) have in covered/uncovered
areas. The board area consists of "no glass", "1-layer glass",
"2-layer glass" parts. If you imagine a simple cloth fabric, you would
know what I mean. The best material has the smallest percentage of "no
glass" area and the largest percentage of "2-layer glass" area, that
would be the most uniform (logically thinking).
"If not, how can I guarantee that the right type of weave was indeed
selected when building my board?"
- instead of "they" building your stackup and board, you have to
determine the stackup before they manufacture it. If you just let fabs
and who knows who manufacture whatever for your board designs, then
many things can go wrong.
Regards,
Istvan Nagy
-----Original Message----- From: Boris Bakshan
Sent: Sunday, December 27, 2015 10:16 PM
To: si-list@xxxxxxxxxxxxx <mailto:si-list@xxxxxxxxxxxxx>
Subject: [SI-LIST] Glass Weave effects and Cross sectioning
Hi experts,
I've been reading much on glass weave effects and its contribution on
skew.
If I encounter a skew problem, can I say anything on weave type
,whether it is mechanically spread or not by doing a cross section of
my traces?
If not, how can I guarantee that the right type of weave was indeed
selected when building my board?
Thank you all!
------------------------------------------------------------------ To
unsubscribe from si-list:
si-list-request@xxxxxxxxxxxxx <mailto:si-list-request@xxxxxxxxxxxxx>
with 'unsubscribe' in the Subject field
or to administer your membership from a web page, go to:
//www.freelists.org/webpage/si-list
For help:
si-list-request@xxxxxxxxxxxxx <mailto:si-list-request@xxxxxxxxxxxxx>
with 'help' in the Subject field
List forum is accessible at:
http://tech.groups.yahoo.com/group/si-list
List archives are viewable at:
//www.freelists.org/archives/si-list
Old (prior to June 6, 2001) list archives are viewable at:
http://www.qsl.net/wb6tpu
--- This email has been checked for viruses by Avast antivirus
------------------------------------------------------------------https://www.avast.com/antivirus
------------------------------------------------------------------ To
unsubscribe from si-list:
si-list-request@xxxxxxxxxxxxx <mailto:si-list-request@xxxxxxxxxxxxx>
with 'unsubscribe' in the Subject field
or to administer your membership from a web page, go to:
//www.freelists.org/webpage/si-list
For help:
si-list-request@xxxxxxxxxxxxx <mailto:si-list-request@xxxxxxxxxxxxx>
with 'help' in the Subject field
List forum is accessible at:
http://tech.groups.yahoo.com/group/si-list
List archives are viewable at:
//www.freelists.org/archives/si-list
Old (prior to June 6, 2001) list archives are viewable at:
http://www.qsl.net/wb6tpu
---
This email has been checked for viruses by Avast antivirus software.
https://www.avast.com/antivirus
------------------------------------------------------------------
To unsubscribe from si-list:
si-list-request@xxxxxxxxxxxxx <mailto:si-list-request@xxxxxxxxxxxxx>
with 'unsubscribe' in the Subject field
or to administer your membership from a web page, go to:
//www.freelists.org/webpage/si-list
For help:
si-list-request@xxxxxxxxxxxxx <mailto:si-list-request@xxxxxxxxxxxxx>
with 'help' in the Subject field
List forum is accessible at:
http://tech.groups.yahoo.com/group/si-list
List archives are viewable at:
//www.freelists.org/archives/si-list
Old (prior to June 6, 2001) list archives are viewable at:
http://www.qsl.net/wb6tpu
---
This email has been checked for viruses by Avast antivirus software.
https://www.avast.com/antivirus
_____
<https://www.avast.com/antivirus>
This email has been checked for viruses by Avast antivirus software.
www.avast.com <https://www.avast.com/antivirus>
------------------------------------------------------------------
To unsubscribe from si-list:
si-list-request@xxxxxxxxxxxxx with 'unsubscribe' in the Subject field
or to administer your membership from a web page, go to:
//www.freelists.org/webpage/si-list
For help:
si-list-request@xxxxxxxxxxxxx with 'help' in the Subject field
List forum is accessible at:
http://tech.groups.yahoo.com/group/si-list
List archives are viewable at:
//www.freelists.org/archives/si-list
Old (prior to June 6, 2001) list archives are viewable at:
http://www.qsl.net/wb6tpu
--
best wishes,
Jun Zhang
------------------------------------------------------------------
To unsubscribe from si-list:
si-list-request@xxxxxxxxxxxxx with 'unsubscribe' in the Subject field
or to administer your membership from a web page, go to:
//www.freelists.org/webpage/si-list
For help:
si-list-request@xxxxxxxxxxxxx with 'help' in the Subject field
List forum is accessible at:
http://tech.groups.yahoo.com/group/si-list
List archives are viewable at:
//www.freelists.org/archives/si-list
Old (prior to June 6, 2001) list archives are viewable at:
http://www.qsl.net/wb6tpu
------------------------------------------------------------------
To unsubscribe from si-list:
si-list-request@xxxxxxxxxxxxx with 'unsubscribe' in the Subject field
or to administer your membership from a web page, go to:
//www.freelists.org/webpage/si-list
For help:
si-list-request@xxxxxxxxxxxxx with 'help' in the Subject field
List forum is accessible at:
http://tech.groups.yahoo.com/group/si-list
List archives are viewable at:
//www.freelists.org/archives/si-list
Old (prior to June 6, 2001) list archives are viewable at:
http://www.qsl.net/wb6tpu
---
This email has been checked for viruses by Avast antivirus software.
https://www.avast.com/antivirus
------------------------------------------------------------------
To unsubscribe from si-list:
si-list-request@xxxxxxxxxxxxx with 'unsubscribe' in the Subject field
or to administer your membership from a web page, go to:
//www.freelists.org/webpage/si-list
For help:
si-list-request@xxxxxxxxxxxxx with 'help' in the Subject field
List forum is accessible at:
http://tech.groups.yahoo.com/group/si-list
List archives are viewable at:
//www.freelists.org/archives/si-list
Old (prior to June 6, 2001) list archives are viewable at:
http://www.qsl.net/wb6tpu
To unsubscribe from si-list:
si-list-request@xxxxxxxxxxxxx with 'unsubscribe' in the Subject field
or to administer your membership from a web page, go to:
//www.freelists.org/webpage/si-list
For help:
si-list-request@xxxxxxxxxxxxx with 'help' in the Subject field
List forum is accessible at:
http://tech.groups.yahoo.com/group/si-list
List archives are viewable at:
//www.freelists.org/archives/si-list
Old (prior to June 6, 2001) list archives are viewable at:
http://www.qsl.net/wb6tpu
------------------------------------------------------------------
To unsubscribe from si-list:
si-list-request@xxxxxxxxxxxxx with 'unsubscribe' in the Subject field
or to administer your membership from a web page, go to:
//www.freelists.org/webpage/si-list
For help:
si-list-request@xxxxxxxxxxxxx with 'help' in the Subject field
List forum is accessible at:
http://tech.groups.yahoo.com/group/si-list
List archives are viewable at:
//www.freelists.org/archives/si-list
Old (prior to June 6, 2001) list archives are viewable at:
http://www.qsl.net/wb6tpu